Description
310s / 1.4845 Stainless Steel Sheet
310s is one of the most high temperature resistant materials
Alternative grades of equivalent materials
| China * GB | GB24511 | S31008 |
| Japan | JIS | SUS310S |
| United States of America | ASTM | 310S |
| UNS | S31008 | |
| South Korea | KS | STS310S |
| European Union | BSEN | 1.4845 |
| India | IS | – |
| Australia | AS | 310S |
| Taiwan, China | CNS | 310S |
| Germany | DIN | X8CrNi25-21 |
| United Kingdom | BS970 BS1449 | – |
| Belgium | BS970Part1 | – |
General Properties
Alloy 310 (UNS S31000) is an austenitic stainless steel developed for use in high temperature corrosion resistant applications. The alloy resists oxidation up to 2010oF (1100oC) under mildly cyclic conditions.
Because of its high chromium and moderate nickel content, Alloy 310 is resistant to sulfidation and can also be used in moderately carburizing atmospheres.
The more severe carburizing atmospheres of thermal process equipment usually require nickel alloys such as 330 (UNS N08330). Alloy 310 can be utilized in slightly oxidizing, nitriding, cementing and thermal cycling applications, albeit, the maximum service temperature must be reduced. Alloy 310 also finds usage in cryogenic applications with low magnetic permeability and toughness down to -450oF (-268oC). When heated between 1202 – 1742oF (650 – 950oC) the alloy is subject to sigma phase precipitation. A solution annealing treatment at 2012 – 2102oF (1100 – 1150oC) will restore a degree of toughness.
310S (UNS S31008) is the low carbon version of the alloy. It is utilized for ease of fabrication. 310H (UNS S31009) is a high carbon modification developed for enhanced creep resistance. In most instances the grain size and carbon content of the plate can meet both the 310S and 310H requirements.
Alloy 310 can be easily welded and processed by standard shop fabrication practices.
Applications
- Cryogenic Components
- Food Processing
- Furnaces – burners, doors, fans, piping and recuperators
- Fluidized Bed Furnaces – coal combustors, grids, piping, wind boxes
- Ore Processing/Steel Plants – smelter and steel melting equipment, continuous casting equipment
- Petroleum Refining – catalytic recovery systems, flares, recuperators, tube hangers
- Power Generation – coal gasifier internals, pulverized coal burners, tube hangers
- Sintering/Cement Plants – burners, burner shields, feeding and discharging systems, wind boxes
- Thermal Processing – annealing covers and boxes, burner grids, doors, fans, muffles and retorts, recuperators, walking beams
Standards
ASTM……..A 240
ASME……..SA 240
AMS……….5521
Corrosion Resistance
Wet Corrosion
Alloy 310 is not designed for service in wet corrosive environments. The high carbon content, which is present to enhance creep properties, has a detrimental effect on aqueous corrosion resistance. The alloy is prone to intergranular corrosion after long term exposure at high temperatures. However, due to its high chromium content (25%), Alloy 310 is more corrosion resistant than most heat resistant alloys.
High Temperature Corrosion
The high chromium (25%) and silicon (0.6%) content of Alloy 310 make it more resistant to high temperature corrosion in most in-service environments. Operating temperatures are listed below.
Oxidizing conditions (max sulfur content – 2 g/m3)
1922°F (1050°C) continuous service
2012°F (1100°C) peak temperature
Oxidizing conditions (max sulfur greater than 2 g/m3)
1742°F (950°C) maximum temperature
Low oxygen atmosphere (max sulfur content – 2 g/m3)
1832°F (1000°C) maximum temperature
Nitriding or carburizing atmospheres
1562 – 1742°F (850 – 950°C) maximum
The alloy does not perform as well as Alloy 600 (UNS N06600) or Alloy 800 (UNS N08800) in reducing, nitriding or carburizing atmospheres, but it does outperform most heat resistant stainless steels in these conditions.
Creep Properties
Typical Creep Properties
| Temperature | Creep Strain (MPa) | Creep Rupture (MPa) | |||||
|---|---|---|---|---|---|---|---|
| °C | °F | 1000 H | 10000 H | 100000 H | 1000 H | 10000 H | 100000 H |
| 600 | 1112 | 120 | 100 | 40 | 200 | 140 | 80 |
| 700 | 1292 | 50 | 35 | 20 | 80 | 45 | 20 |
| 800 | 1472 | 20 | 10 | 8 | 35 | 20 | 8 |
| 900 | 1652 | 10 | 6 | 3 | 15 | 10 | 5 |
| 1000 | 1832 | 5 | 3 | 1.5 | 9 | 4 | 2 |
Chemical Analysis
Weight % (all values are maximum unless a range is otherwise indicated)
| Element | 310 | 310S | 310H |
|---|---|---|---|
| Chromium | 24.0 min.-26.0 max. | 24.0 min.-26.0 max. | 24.0 min.-26.0 max. |
| Nickel | 19.0 min.-22.0 max. | 19.0 min.-22.0 max. | 19.0 min.-22.0 max. |
| Carbon | 0.25 | 0.08 | 0.40 min. – 0.10 max. |
| Manganese | 2.00 | 2.00 | 2.00 |
| Phosphorus | 0.045 | 0.045 | 0.045 |
| Sulfer | 0.030 | 0.030 | 0.030 |
| Silicon | 1.50 | 1.50 | 0.75 |
| Iron | Balance | Balance | Balance |
Physical Properties
Density
0.285 lbs/in3
7.89 g/cm3
Specific Heat
0.12 BTU/lb-°F (32 – 212°F)
502 J/kg-°K (0 – 100°C)
Modulus of Elasticity
28.5 x 106 psi
196 GPa
Thermal Conductivity 212°F (100°C)
8.0 BTU/hr/ft2/ft/°F
10.8 W/m-°K
Melting Range
2470 – 2555°F
1354 – 1402°C
Electrical Resistivity
30.7 Microhm-in at 68°C
78.0 Microhm-cm at 20°C
Mechanical Properties
Typical Values at 68°F (20°C)
| Yield Strength 0.2% Offset |
Ultimate Tensile Strength |
Elongation in 2 in. |
Hardness | ||
|---|---|---|---|---|---|
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
| 35,000 | 245 | 80,000 | 550 | 45 | 217 Brinell |
Fabrication Data
Fabrication Data Alloy 310 can be easily welded and processed by standard shop fabrication practices. Hot Forming Heat uniformly at 1742 – 2192°F (950 – 1200°C). After hot forming a final anneal at 1832 – 2101°F (1000 – 1150°C) followed by rapid quenching is recommended. Cold Forming The alloy is quite ductile and forms in a manner very similar to 316. Cold forming of pieces with long-term exposure to high temperatures is not recommended since the alloy is subject to carbide precipitation and sigma phase precipitants. Welding Alloy 310 can be readily welded by most standard processes including TIG, PLASMA, MIG, SMAW, SAW and FCAW.
Contact Us Now!
Our products: stainless steel including all sizes of steel coils, steel sheets, steel pipes, flat steel, angle steel, round steel, channel steel and other metal materials.
If you need product information or price, please fill in your contact information in the form below, we will usually contact you within 12 hours. You can also click on our email address info@sinosteel.ltd to send us an email to get prompt reply.
Send me the inquiry,free samples and the most favorable quotation are waiting for you!
Supply Better Material for Project & Find Best Solution for Clients
Wish your business boom and all the best!